High-quality InN grown on KOH wet etched N-polar InN template by RF-MBE

We have succeeded in dramatically decreasing the density of dislocations in InN by regrowing InN films on micro-facetted N-polar InN templates. The micro-facetted N-polar InN templates were formed by wet etching in a 10 mol/l KOH solution. InN films were regrown on the micro-facetted N-polar InN templates and on flat surface N-polar InN templates for comparison by radio-frequency plasma-assisted molecular beam epitaxy. InN regrown on micro-facetted InN had considerably smaller twist distribution than that grown on the flat InN templates. From transmission electron microscopy observation, it was confirmed that the InN grown on the micro-facetted InN template had much lower density of dislocations than that grown on the flat InN template, and moreover the propagation of edge dislocations was almost completely terminated at the interface between the regrown InN and the micro-facetted InN template. Based on the results, we propose that regrowth of InN on micro-facetted InN templates is an effective way to obtain high-quality InN films. (© 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)