Corrosion, 3. Corrosion Protection and Testing

1.	Corrosion Protection by Coating
1.1.	Metal Coatings
1.2.	Inorganic Nonmetallic Protective Coatings
1.2.1.	Enamel
1.2.2.	Brick Lining
1.2.3.	Thermally Sprayed Coatings
1.3.	Organic Lining and Coating Materials
1.3.1.	Rubber Linings
1.3.2.	Rubber-Plastic Composite Linings
1.3.3.	Linings Consisting of Thermally Crosslinkable Thermosetting Plastics
1.3.4.	Reinforced Reaction Resin Coatings, Crosslinkable with Catalysts
1.3.5.	Thermoplastic Linings
1.3.6.	Paints and Powder Coatings
2.	Inhibitors
3.	Electrochemical Corrosion Protection
4.	Corrosion Testing
4.1.	Introduction
4.2.	Test Methods

References

1 J. Möller, Metall 26 (1972) 820–825.
Web of Science® Google Scholar
2 J. Möller, Ind. Anz. 96 (1974) no. 38, 856–857.
Google Scholar
3 U. Richter, Schweißtechnik 7 (1975) 116–120.
Google Scholar
4 DIN EN 1011-5, Verbindungsschweißen plattierter Stähle, Beuth Verlag, Berlin 2003.
Google Scholar
5 U. Richter, Schweißen & Schneiden 25 (1973) 218–220.
Google Scholar
6 J. Chene, P. Luginbühl, 96 Tech. Rundsch. Sulzer 2 (1973) 73–78.
Google Scholar
7 W. Ruckdeschel, Schweißtechnik 63 (1973) 229–241.
Google Scholar
8 B. Bouaifi, J. Krohn, U. Draugelates, DECHEMA-Monogr. 103 (1986) 165–175.
Google Scholar
9 B. Bouaifi, I. Graf, U. Draugelates, Prakt. Metallogr. 25 (1988) no. 11, 543–554.
Google Scholar
10 D. Fuchs, H. Preisendanz, P. Schüler, DEW-Tech. Ber. 13 (1973) 137–142.
CAS Google Scholar
11 Pfaudler-Werke AG, Data Sheet 249–1: “Resista-Clad, ein Verfahren, das Metalle dauerhaft verbindet”, 1988.
Google Scholar
12 Pfaudler Company, Data-Sheet DS49–300–1: “Resista-Clad, Weld-Bonded Cladding Process”, 1984.
Google Scholar
13 Pfaudler Company, Data-Sheet DS49–301–1: “Resista-Clad, Physical & Chemical Performance Data”, 1985.
Google Scholar
14 M.X. Cerny, Power Eng. (1987) no. 8, 36–37.
Web of Science® Google Scholar
15 W. Burckhardt, Technik 26 (1971) 697–704;
Google Scholar
27 (1972) 563–570, 528–531;
Google Scholar
30 (1975) 239–245.
Google Scholar
16 L.L. Shreir, Ind. Finish 8 (1955) 261–267, 389–400.
Google Scholar
17 L. Winkler, Metall 31 (1977) 506–509.
Web of Science® Google Scholar
18 J. Wurm, DECHEMA-Monogr. 76 (1974) 1486–1504, 81–89.
Google Scholar
19 A.W. Berger, CAV (1980) 82–84.
Google Scholar
20 K. Breitwieser, R. Engelmann, Maschinenmarkt 85 (1979) 393–400.
Google Scholar
21 W. Paatsch, Metall 30 (1976) 332–336.
Web of Science® Google Scholar
22 H. Gräfen, VDI-Ber. 624 (1986) 273.
Google Scholar
23 H. Gräfen: “Werkstoffe des Chemieanlagenbaus, Stand der Entwicklung”, in 50 Jahre Werkstofftechnik an der Fakultät für Maschinenwesen, Colloquium at the Technische Universität München, 1989, pp. 38–63.
Google Scholar
24 K. Kreisel, E. Protogerakis, DECHEMA-Monogr. 103 (1986) 191–205.
Google Scholar
25 H. Schindler: Nichtmetallische Werkstoffe für die Chemietechnik, Fortschritte der Verfahrenstechnik, vol. 15, VDI-Verlag GmbH, Düsseldorf 1977, pp. 445–459.
Google Scholar
26 H. Schindler: Nichtmetallische Werkstoffe für die Chemietechnik, Fortschritte der Verfahrenstechnik, vol. 18, VDI-Verlag GmbH, Düsseldorf 1980, pp. 439–456.
Google Scholar
27 H. Gräfen, U. Gramberg, H. Schindler, Werkst. Korros. 30 (1979) 297–307.
10.1002/maco.19790300502
Web of Science® Google Scholar
28 A.H. Dietzel: Emaillierung, Springer Verlag, Berlin 1981.
10.1007/978-3-642-50978-0
Google Scholar
29 R. Lorentz: “Korrosion von Chemieemail durch wäßrigneutrale Medien“, Mitteilungen des Vereins Deutscher Emailfachleute e.V., vol. 34/5, (1986) 65–76.
Google Scholar
30 H. Scharbach: “Glas- und Glaskeramikemail für den technischen Einsatz”, Swiss Chem. 5 (1983) 55–60.
Google Scholar
31 Pfaudler-Werke AG, Schwetzingen, printed publication FCP5M 12/87.
Google Scholar
32 Literature supplied by Pfaudler-Werke AG, Schwetzingen, at ACHEMA 1988 in Frankfurt.
Google Scholar
33 E. Kreisel, E. Protogerakis: “Thermisches Spritzen in Chemieapparate-Maschinenbau-Anlagen, Werkstoffe, Anwendungen,” Chem. Ing. Tech. 59 (1987) no. 2, 118–122.
10.1002/cite.330590206
CAS Web of Science® Google Scholar
34 Sigri GmbH, Meitingen, printed publication 853 01 10, 1983.
Google Scholar
35 K.H. Möbius: “Füllstoffhaltige elektrisch leitfähige Kunststoffe”, Kunststoffe 78 (1988) no. 1, 53–58.
Web of Science® Google Scholar
36 A. Malliaris, D.T. Turner: “Influence of Particle Size on the Electrical Resistivity of Compacted Mixtures of Polymeric and Metallic Powders”, J. Appl. Phys. 42 (1971) no. 2, 614–618.
10.1063/1.1660071
CAS ADS Web of Science® Google Scholar
37 H. Schindler, H. Gräfen, Chem. Ing. Tech. 57 (1985) no. 7, 597–602.
10.1002/cite.330570706
CAS Web of Science® Google Scholar
38 H. Gräfen: “Fortschritte beim Einsatz organischer Werkstoffe im Korrosionsschutz”, VDI-Ber. 670 (1988) 451–468.
Google Scholar
39 E. Oelke: Kunststoffe in Chemieanlagen, VDI-Gesellschaft Kunststofftechnik, VDI-Verlag GmbH, Düsseldorf 1986, pp. 167–183.
Google Scholar
40 T. Hasky in: Oberflächenschutz mit organischen Werkstoffen im Behälter-, Apparate- und Rohrleitungsbau, VDI-Gesellschaft Werkstofftechnik, VDI-Verlag GmbH, Düsseldorf 1980, pp. 101–129.
Google Scholar
41 E. Schacht: “Erfahrungen mit Gummierungen und Beschichtungen in Anlagen zur Rauchgasentschwefelung”, VDI-Ber. 674 (1988) 263–281.
CAS Google Scholar
42 A. Swozil, G. Ullmann, Chem. Ing. Tech. 52 (1980) no. 4, 292–298.
10.1002/cite.330520403
CAS Web of Science® Google Scholar
43 J.E. Niesse: “Innovations in Organic Linings”, Chem. Eng. Prog. 82 (1986) no. 6, 55–62.
Web of Science® Google Scholar
44 G. Dexheimer, H. Schindler, internal report, Bayer AG, 1989.
Google Scholar
45 Steuler Industriewerke, “Bekaplast-Säureschutzverkleidung”, company brochure, , Höhr-Grenzhausen 1970.
Google Scholar
46 H.R. Rottkämer in: E. Heitz, W. Schwenk, Werkst. Korros. 27 (1976), 169–184.
Google Scholar
47 J.I. Bregmann: Corrosion Inhibitors, The Macmillan Comp., New York 1963.
Google Scholar
48 H.J. Rother: Die Praxis des Korrosionsschutzes, Corrosion Inhibitors, The Maxmillan Comp., New York 1963, pp. 250–266.
Google Scholar
49 H. Fischer, Werkst. Korros. 23 (1972) 445–465.
10.1002/maco.19720230602
CAS Google Scholar
50 K. Risch, Werkst. Korros. 25 (1974) 727–734.
10.1002/maco.19740251006
CAS Google Scholar
51 E. Rabald, Werkst. Korros. 5 (1954) 368–392.
10.1002/maco.19540051004
CAS Google Scholar
52 Corrosion Inhibition, Proceedings of the Int. Conference on Corrosion Inhibition, NACE Houston 1988.
Google Scholar
53 D. Kuron, H.-J. Rother, R. Holm, S. Storp, Werkst. Korros. 37 (1986) 83–93.
10.1002/maco.19860370205
CAS Web of Science® Google Scholar
54 M.N. Desai, Werkst. Korros. 23 (1972) 483–487.
10.1002/maco.19720230606
CAS Google Scholar
55 M.N. Desai, Werkst. Korros. 24 (1973) 707–716.
10.1002/maco.19730240807
CAS Google Scholar
56 J.C. Kora, S.C. Makwana, K.C. Koshel, N.K. Patel, Werkst. Korros. 25 (1974) 753–756.
10.1002/maco.19740251011
Google Scholar
57 M. Brooke, Chem. Eng. 12 (1954) 230–234.
Google Scholar
58 D. Kuron, H.J. Rother, H. Gräfen, Werkst. Korros. 32 (1981) 409–421.
10.1002/maco.19810321002
CAS Web of Science® Google Scholar
59 G. Schmitt, B. Olbertz, Werkst. Korros. 29 (1978) 451–456;
10.1002/maco.19780290704
CAS Web of Science® Google Scholar
G. Schmitt, B. Olbertz, Werkst. Korros. 35 (1984) 99–106;
10.1002/maco.19840350302
CAS Web of Science® Google Scholar
G. Schmitt, B. Olbertz, K.H. Kurtz, Werkst. Korros. 35 (1984) 107–110.
10.1002/maco.19840350303
CAS Web of Science® Google Scholar
60 I. Class, Werkst. Korros. 6 (1955) 237–245.
10.1002/maco.19550060505
CAS Google Scholar
61 H. Gräfen, G. Herbsleb, F. Paulekat, W. Schwenk, Werkst. Korros. 22 (1971) 16–31.
10.1002/maco.19710220104
Google Scholar
62 E.-M. Horn, R. Kilian, H. Stiepel, H. Gräfen, Werkst. Korros. 23 (1972) 967–973.
10.1002/maco.19720231103
CAS Google Scholar
63 J.-W. Kühn, V. Burgsdorff, H. Richter, in W. v. Baeckmann, W. Schwenk (eds.): Handbuch des kathodischen Korrosionsschutzes, Verlag Chemie, Weinheim 1971, pp. 342–354.
Google Scholar
64 H. Gräfen, U. Heinzelmann, F. Paulekat, in W. v. Baeckmann, W. Schwenk, W. Prinz (eds.): Handbuch des kathodischen Korrosionsschutzes, Verlag Chemie, Weinheim, 1971, pp. 431–458.
Google Scholar
65 J. Küpper-Feser, R. Feser, G. Franke, W. Bytyn, EUROCORR European Corrosion Congress, Estoril, Portugal, September 2013.
Google Scholar
66 W. Bytyn,, G. Franke, Materials and Corrosion 53 (2002) no. 8, 568–578.
10.1002/1521-4176(200208)53:8<568::AID-MACO568>3.0.CO;2-H
CAS Web of Science® Google Scholar
67 W.P. Banks, J.P. Sudbury, Corrosion 19 (1963) 300–307.
Google Scholar
68 J.M. Stammen, Mater. Proc. 7 (1968) no. 12, 33–35.
Web of Science® Google Scholar
69 F. Paulekat, H. Gräfen, D. Kuron, Werkst. Korrosion 33 (1982) 254–262.
10.1002/maco.19820330503
CAS Web of Science® Google Scholar
70 D. Kuron, H. Gräfen, Chem. Ing. Tech. 60 (1988) 604–612.
10.1002/cite.330600807
CAS Web of Science® Google Scholar
71 H. Gräfen, D. Kuron, Arch. Eisenhüttenwes. 36 (1965) 285–291.
10.1002/srin.196504083
Google Scholar
72 H. Gräfen et al., Werkst. Korros. 22 (1971) 16–31.
10.1002/maco.19710220104
Google Scholar
73 J.B. Cotton, Werkst. Korros. 11 (1960) 152–155.
10.1002/maco.19600110304
CAS Google Scholar
74 Verein Deutscher Eisenhüttenleute (ed.): Prüfung und Untersuchung der Korrosionsbeständigkeit von Stählen, Verlag Stahleisen, Düsseldorf 1973.
Google Scholar
75 DIN Taschenbuch 219, Korrosion und Korrosionsschutz, Beuth Verlag, Berlin 2015.
Google Scholar
76 H. Gräfen, G. Herbsleb, in: H. Gräfen, F. Kahl, A. Rahmel (eds.): 1. Korrosionum, die Bedeutung der Korrosion für Planung, Bau und Betrieb von Anlagen der chemischen und petrochemischen Technik sowie der Mineralölindustrie, Verlag Chemie, Weinheim 1974, pp. 55–69.
Google Scholar
77 DIN 50 905: Korrosion der Metalle. Korrosionsuntersuchungen Part 1 Grundsätze; Part 2 Korrosionsgrößen bei gleichmäßiger Flächenkorrosion; Part 3 Korrosionsgrößen bei ungleichmäßiger und örtlicher Korrosion ohne mechanische Belastung; Part 4 Durchführung von chemischen Korrosionsversuchen ohne mechanische Belastung in Flüssigkeiten im Laboratorium, Beuth Verlag, Berlin 1987.
Google Scholar
78 ASTM G 4–84: Standard Method for Conducting Corrosion Coupon Tests in Plant Equipment (1984).
Google Scholar
79 ASTM G 31–72: Standard Practice for Laboratory Immersion Corrosion Testing of Metals (1985).
Google Scholar
80 ASTM G 78–83: Standard Guide for Crevice Corrosion Testing of Iron-Base and Nickel-Base Stainless Alloys in Seawater and other Chloride Containing Aqueous Environments (1983).
Google Scholar
81 DIN 50 915: Prüfung von unlegierten und niedriglegierten Stählen auf Beständigkeit gegen interkristalline Spannungsrißkorrosion, Beuth Verlag, Berlin 1985.
Google Scholar
82 ASTM G 30–79: Standard Practice for Making and Using U-Bend Stress-Corrosion Test-Specimens (1984).
Google Scholar
83 ASTM G 38–73: Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens (1984).
Google Scholar
84 K. Risch, Werkst. Korros. 36 (1985) 55–63.
10.1002/maco.19850360202
CAS Web of Science® Google Scholar
85 DIN 50 920: Korrosion der Metalle. Korrosionsuntersuchungen in strömenden Flüssigkeiten. Part 1 Allgemeines, Beuth Verlag, Berlin 1985.
Google Scholar
86 DIN 50 914: Prüfung nichtrostender Stähle auf Beständigkeit gegen interkristalline Korrosion. Kupfersulfat-Schwefelsäure-Verfahren. Strauß-Test, Beuth Verlag, Berlin 1984.
Google Scholar
87 Stahl-Eisen-Prüfblatt 1877: Prüfung der Beständigkeit hochlegierter, korrosionsbeständiger Werkstoffe gegen interkristalline Korrosion, VDEh, 1979.
Google Scholar
88 DIN 50 921: Korrosion der Metalle, Prüfung nichtrostender austenitischer Stähle auf Beständigkeit gegen örtliche Korrosion in stark oxidierenden Säuren. Korrosionsversuch in Salpetersäure durch Messung des Massenverlustes (Prüfung nach Huey), Beuth Verlag, Berlin 1984.
Google Scholar
89 ASTM A 262–86: Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels (1986).
Google Scholar
90 Europäische Kommission, Euronorm 114–72, Ermittlung der Beständigkeit nichtrostender austenitischer Stähle gegen interkristalline Korrosion: Korrosionsversuch in Schwefelsäure-Kupfersulfatlösung (Prüfung nach Monypenny-Strauβ), 1972.
Google Scholar
91 ASTM G 28–85: Standard Test Methods of Detecting Susceptibility to Intergranular Attack in Wrought, Nickel-Rich, Chromium-Bearing Alloys (1985).
Google Scholar
92 ASTM G 48–76: Standard Test Methods for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys by the Use of Ferric Chloride Solution (1980).
Google Scholar
93 ASTM G 36–87: Standard Practice for Evaluating Stress-Corrosion-Cracking Resistance of Metals and Alloys in a Boiling Magnesium Chloride Solution (1987).
Google Scholar
94 ASTM G 44–88: Standard Practice for Evaluating Stress Corrosion Cracking Resistance of Metals and Alloys by Alternate Immersion in 3.5 % Sodium Chloride Solution (1988).
Google Scholar
95 NACE Standard TM-01–077, The NACE Testing Methods For Analysis of Stress Corrosion Cracking in H₂S Environments, G2MT Labs.
Google Scholar
96 DIN 50 916: Prüfung von Kupferlegierungen. Spannungsrißkorrosionsversuche mit Ammoniak. Part 1 Prüfung von Rohren, Stangen und Profilen, Beuth Verlag, Berlin 1976; Part 2 Prüfung von Bauteilen, Beuth Verlag, Berlin 1985.
Google Scholar
97 ASTM G 37–85: Standard Test Method for Use of Mattsson's Solution of pH 7.2 to Evaluate the Stress-Corrosion Cracking Susceptibility of Copper-Zinc Alloys (1985).
Google Scholar
98 ASTM G 47–79: Standard Test Method for Determining Susceptibility to Stress-Corrosion Cracking of High-Strength Aluminum Alloy Products (1984).
Google Scholar
99 DIN 50 917: Korrosion der Metalle. Naturversuche. Freibewitterung, Beuth Verlag, Berlin 1979.
Google Scholar
100 DIN 50 017: Klimate und ihre technische Anwendung. Kondenswasser-Prüfklimate, Beuth Verlag, Berlin 1982.
Google Scholar
101 DIN 50 018: Korrosionsprüfungen. Beanspruchung im Kondenswasser-Wechselklima mit schwefeldioxidhaltiger Atmosphäre, Beuth Verlag, Berlin 1978.
Google Scholar
102 DIN 50 021: Korrosionsprüfungen. Sprühnebelprüfungen mit verschiedenen Natriumchloridlösungen, Beuth Verlag, Berlin 1975.
Google Scholar
103 ASTM B 117–85: Standard Method of Salt Spray (Fog) Testing (1985).
Google Scholar
104 ASTM G 87–84: Standard Practice for Conducting Moist SO₂ Tests (1984).
Google Scholar
105 ASTM G 91–86: Standard Practice for Monitoring Atmospheric SO₂ Using the Sulfation Plate Technique (1986).
Google Scholar
106 ASTM G 85–85: Standard Practice for Modified Salt Spray (Fog) Testing (1985).
Google Scholar
107 DIN 50 918: Korrosion der Metalle. Elektrochemische Korrosionsuntersuchungen, Beuth Verlag, Berlin 1978.
Google Scholar
108 ASTM G 3–74: Standard Practice for Conventions Applicable to Electrochemical Measurements in Corrosion Testing (1981).
Google Scholar
109 ASTM G 5–87: Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements (1987).
Google Scholar
110 DIN 50 919: Korrosion der Metalle. Korrosionsuntersuchungen der Kontaktkorrosion in Elektrolytlösungen, Beuth Verlag, Berlin 1984.
Google Scholar
111 ASTM G 71–81: Standard Guide for Conducting and Evaluating Galvanic Corrosion Tests in Electrolytes (1986).
Google Scholar
112 D. Kuron, H. Gräfen, Z. Werkstofftechn. 8 (1977) 182–191.
10.1002/mawe.19770080604
CAS Google Scholar

Corrosion, 3. Corrosion Protection and Testing

View previous versions

Corrosion, 3. Corrosion Protection and Testing

Corrosion

Abstract

References

Further Reading

References

Information

About Wiley Online Library

Help & Support

Opportunities

Connect with Wiley

Corrosion, 3. Corrosion Protection and Testing

View previous versions

Corrosion, 3. Corrosion Protection and Testing

Corrosion

Abstract

References

Further Reading

References

Related

Information