Dislocation structures in aluminium-rich Ni3(Al, Ta) and Ni3(Al, Hf)
Bornova/Izmir, Turkey.
Abstract
enInvestigation of dislocation structures by transmission electron microscopy in the aluminium-rich Ni3(Al, Ta) and Ni3(Al, Hf) intermetallic phases shows the presence of dislocations close to the〈111〉 crystallographic direction, in addition to the dislocations along the 〈110〉 direction. The{110} and/or{112} planes are suggested to be the possible slip planes for the 〈111〉 type dislocations, assuming that the dislocations have the b = a[110] type Burgers vector. Dislocations at low temperatures are mainly straight and parallel to each other. However, at high temperatures dislocations lose their straightness. Two distinct dipoles are observed at low temperatures, namely〈111〉 and 〈110〉 oriented dislocations. Formation of dipoles and jogs is investigated also.
Abstract
deUntersuchungen der Versetzungsstruktur mittels Elektronenmikroskopie in Al-reichen intermetallischen Ni3(Al, Ta)- und Ni3(Al, Hf)-Phasen haben zusätzlich zu Versetzungen in 〈110〉 -Richtung das Vorhandensein von Versetzungen ergeben, die etwa in der kristallographischen 〈111〉 -Richtung liegen. Es wird angenommen, daß die{110}- und/oder{112}-Ebenen mögliche Gleitebenen für die 〈111〉 -Versetzungen sind, wobei angenommen wird, daß die Versetzungen einen Burgersvektor mit b = a[110] besitzen. Versetzungen bei tiefen Temperaturen sind hauptsächlich gerade und parallel zueinander. Jedoch verlieren die Versetzungen ihre Geradheit bei hohen Temperaturen. Zwei unterschiedliche Dipole werden bei niedrigen Temperaturen beobachtet, 〈111〉 - und 〈110〉 -orientierte Versetzungen. Die Bildung von Dipolen und Knoten wird ebenfalls untersucht.