Enrichment of Gold in Low Grade Copper Matte from Arsenical Refractory Gold Concentrate via Matte Smelting Method

To solve the problem of low leaching ratio of direct gold cyanide leaching from arsenical refractory gold concentrate, this paper proposed a matte smelting process for gold enrichment in low grade copper matte. The effects of copper content in the mixed material, ratio change in slag type, smelting temperature and reaction time on recovery rate of gold and copper were investigated. The experimental results indicated that the recovery rate of gold increased with the increase of copper content in the mixed materials, temperature and reaction time. It was also noted that the recovery rate of gold and copper were respectively 98.16% and 96.39% when the addition of copper content in the mixed material was 3%, slag type of CaO/SiO₂ and FeO/SiO₂ were 0.6 and 0.9 in 1250°C and the time of reaction was 40min. Most of the arsenic was oxidized into As2O3 existed in the dust. The results showed that the matte smelting method can achieve efficient recovery of gold from arsenical refractory gold concentrate.

References

T.Z. Yang. Metallurgy and deep production of noble metal (Changsha: Central south university press, 2005).
Google Scholar
T.N. Angelidis and K.A. Kydros, “Selective gold dissolution from a roasted auriferous pyrite-arsenopyrite concentrate,” Hydrometallurgy, 37 (1) (1995), 75-88.
10.1016/0304-386X(94)00020-4
CAS Web of Science® Google Scholar
Q.C. Li, D.X. Li, and F.J. Qian, “Pre-oxidation of high-sulfur and high-arsenic refractory gold concentrate by ozone and ferric ions in acidic media,” Hydrometallurgy, 97 (1–2) (2009), 61-66.
10.1016/j.hydromet.2009.01.002
CAS Web of Science® Google Scholar
J.G. Dunn and A.C. Chamberlain, “The recovery of gold from refractory arsenopyrite concentrates by pyrolysis–oxidation,” Minerals Engineering, 10(9)(1997), 919-928.
10.1016/S0892-6875(97)00074-5
CAS Web of Science® Google Scholar
F.P. Gudyanga et al., “An acidic pressure oxidation pretreatment of refractory gold concentrates from the KweKwe roasting plant, Zimbabwe,” Minerals Engineering, 12(8) (1999), 863-875.
10.1016/S0892-6875(99)00074-6
CAS Web of Science® Google Scholar
T.L. Deng and M.X. Liao, “Gold recovery enhancement from a refractory flotation concentrate by sequential bioleaching and thiourea leach,” Hydrometallurgy, 63 (3) (2002), 249-255.
10.1016/S0304-386X(01)00226-2
CAS Web of Science® Google Scholar
A. Hol et al., “The effect of anaerobic processes on the leach ability of an arsenopyrit refractory ore,” Minerals Engineering, 24 (2011), 535-540.
10.1016/j.mineng.2010.10.001
CAS Web of Science® Google Scholar
J. Liu et al., “Selective arsenic-fixing roast of refractory gold concentrate,” Metallurgical and Materials Transactions B, 31B (2000), 1163-168.
10.1007/s11663-000-0002-6
CAS Web of Science® Google Scholar
P.K. Amankwah and C.A. Pickles, “Microwave roasting of a carbonaceous sulphidic gold concentrate,” Minerals Engineering, 22 (2009), 1095-1101.
10.1016/j.mineng.2009.02.012
CAS Web of Science® Google Scholar
M. Saba et al., “Diagnostic pretreatment procedure for simultaneous cyanide leaching of gold and silver from a refractory gold silver ore,” Minerals Engineering, 24 (2011), 1703-1709.
10.1016/j.mineng.2011.09.013
CAS Web of Science® Google Scholar
G.L. Gao et al., “Kinetics of high-sulfur and high-arsenic refractory gold concentrate oxidation by dilute nitric acid under mild conditions,” Minerals Engineering, 22 (2009), 111-115.
Google Scholar
K.B. Shen, “Research on two stages roast for pretreatment of sulfur & arsenal enriched refractory golden ore,” Yunnan Chemical Technology, 34(5) (2007), 26-29.
Google Scholar
T.S. Qiu, G.H. Nie, and Q. Zhang, “Present situation and development of pretreatment and leaching technology for refractory copper-bearing golden ore,” Gold, 26(8) (2005), 30-34.
Google Scholar
B.S. Kafui Nyavor and Nosa O. Egiebor, “Controlling SO₂ emissions in the roasting of gold concentrate,” JOM, 43 (12) (1991), 32-34.
10.1007/BF03223145
Google Scholar
R.C. Cui et al., “Bacterial oxidation-cyanidation leaching for varied arsenal-bearing golden ore,” Chinese Journal of Nonferrous Metals, 21(3)(2011), 694-699.
Google Scholar
D. Langhans et al, “Biooxidation of an arsenic-bearing refractory gold ore,” Minerals Engineering, 8 (1-2) (1995), 147-158.
10.1016/0892-6875(94)00109-P
Web of Science® Google Scholar
S. Ubaldini et al., “Combined bio-hydrometallurgical process for gold recovery from refractory stibnite,” Minerals Engineering, 13 (14-15) (2000), 1641-1646.
10.1016/S0892-6875(00)00148-5
CAS Web of Science® Google Scholar

7th International Symposium on High‐Temperature Metallurgical Processing