Wear debris-induced inflammation is considered to be the main cause for periprosthetic osteolysis in total hip replacements (THR). The objective of this retrieval study was to examine the tissue reactions and exposure to metal ions and wear particles in periprosthetic tissues and blood samples from patients with titanium (Ti)-based hip prostheses that were revised due to wear, osteolysis, and/or aseptic loosening. Semiquantitative, histological tissue evaluations in 30 THR-patients revealed numerous wear debris-loaded macrophages, inflammatory cells, and necrosis in both groups. Particle load was highest in tissues adjacent to loosened cemented Ti stems that contained mainly submicron zirconium (Zr) dioxide particles. Particles containing pure Ti and Ti alloy elements were most abundant in tissues near retrieved uncemented cups. Polyethylene particles were also detected, but accounted only for a small portion of the total particle number. The blood concentrations of Ti and Zr were highly elevated in cases with high abrasive wear and osteolysis. Our findings indicate that wear particles of different chemical composition induced similar inflammatory responses, which suggests that particle size and load might be more important than the wear particle composition in periprosthetic inflammation and osteolysis. © 2014 The Authors. Journal of Biomedical Materials Research Part B: Applied Biomaterials Published by Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 103B:709–717, 2015.

INTRODUCTION

Total hip replacements (THR) generally have a good clinical outcome in the majority of patients. However, some patients require revision surgery at some stage. Aseptic loosening due to periprosthetic osteolysis is still the major cause for revision.1, 2 Debris generated by wear of the bearing surfaces and loosened components are thought to be the main cause for periprosthetic inflammation leading to osteolysis, which is affected by particle characteristics, such as particle size, load, shape, and chemical reactivity.1-3 It has been found that micrometer and nanometer-sized particulate wear debris is co-localized with inflammatory responses in tissues around loosened implants.4, 5 Adverse local tissue reactions to metal debris, such as lymphocyte infiltration, proinflammatory cytokine release from macrophages, multinuclear giant cell formation and necrosis have mainly been associated with metal-on-metal hip prostheses.6 In addition to local responses, metal debris may spread over the whole body via systemic circulation (i.e., lymph and blood). They have been identified in the macrophages of various distinct organs such as liver and spleen.7 However, the impact of wear debris on these organs is not fully determined.

Degradation products released from metallic implants cannot only occur in the form of particulate wear debris, but also as inorganic metal salts or free metal ions. Metal ions are generated due to physicochemical processes, such as crevice8 and galvanic corrosion, or cellular digestion mechanisms.9 Increased ion release was an early concern with cementless hip prostheses because of the increased surface area of metal in the porous coated designs.10-12 Moreover, measurement of zirconium (Zr) in blood has been proposed as an indicator for bone cement debris degradation and loosening of cemented hip implants, when Zr is present in the polymethylmethacrylate matrix.13 Other implant-derived metal ions such as cobalt (Co), chromium (Cr), and titanium (Ti) have been shown to increase bone resorption and osteoclast differentiation in vitro,14-16 which suggests a contribution of metal ions in the mechanism of osteolysis. Titanium and its alloys are still the most used material for bone fixation with successful osseointegration17 and the level of Ti-ion release is low under normal circumstances.

This retrieval study was conducted to grade the inflammatory tissue reactions and assess the exposure to wear debris and metal ions in tissues surrounding Ti-based hip prostheses. These findings were correlated to systemic and local ion levels recorded in these patients.

MATERIAL AND METHODS

Patients

From our retrieval biobank, we selected blood and tissue samples from 30 patients with Ti-based hip implants that had been revised due to wear, osteolysis, and/or aseptic loosening (Table 1). The retrievals had been consecutively collected in the period of 2008 to 2012 from four hospitals in Norway. We found it convenient to divide the patients in two groups by fixation status of the prosthesis: Fifteen patients had loose cemented stems, but well-fixed cemented cups. The Ti alloy stems (Titan®) were cemented using Palacos bone cement [Palacos G (Schering-Plough), Palacos Refobacin (Merck), Palacos R + G (Heraeus)], containing radio-opaque ZrO₂ particles. The cemented cups showed no sign of failure and were not revised.

Table 1. Patient Data, Implant Duration, and Reasons for Revision

Case No.	Gender, Age at Retrieval (yr)	Duration (months)	Reason for Revision
Uncementeda
1	M, 51	214	Cup loosening
2	F, 70	196	PE wear, pain
3	M, 65	167	Acetabular osteolysis, loosening
4	F, 68	160	Cup loosening
5	F, 78	173	Acetabular osteolysis, cup loosening
6	F, 72	185	Acetabular osteolysis, PE wear
7	F, bNA	228	Acetabular osteolysis, PE wear
8	M, 44	200	PE wear
9	F, 54	174	Acetabular osteolysis, PE wear
10	F, 77	87	PE wear
11	M, 53	167	Acetabular osteolysis, PE wear, pain
12	F, 76	232	Acetabular osteolysis, PE wear
13	M, 70	222	Cup loosening
14	M, 76	220	PE wear, acetabular osteolysis
15	F, 56	200	PE wear, acetabular osteolysis
Cementedc
16	M, 78	69	Femoral osteolysis, stem loosening
17	F, 71	52	Femoral osteolysis, stem loosening
18	F, 50	99	Femoral osteolysis, stem loosening
19	M, 79	70	Femoral osteolysis, stem loosening
20	M, 64	72	Femoral osteolysis, stem loosening
21	M, 73	24	Femoral osteolysis, stem loosening
22	M, 78	97	Femoral osteolysis, stem loosening
23	M, 77	74	Femoral osteolysis, stem loosening
24	M, 69	18	Femoral osteolysis, stem loosening
25	M, 80	105	Femoral osteolysis, stem loosening
26	F, 67	90	Femoral osteolysis, stem loosening
27	F, 76	98	Femoral osteolysis, stem loosening
28	F, 62	141	Femoral osteolysis, stem loosening
29	M, 71	89	Femoral osteolysis, stem loosening
30	bNA, 70	75	Femoral osteolysis, stem loosening

^a Uncemented TiAlV femoral stems (Profile, DePuy) and uncemented metal-backed cups with conventional UHMWPE liners. The head material in these cases was CoCr, except for case nr. 1 (alumina).
^b NA: not available.
^c Cemented femoral stems and PE-liners (TiAlV, Titan®, DePuy). The head materials were mainly CoCr exept for cases: 17, 20, and 28 (alumina).

The other fifteen patients had worn and loose uncemented cups, but well-fixed stems. The uncemented cups that were revised had metal-backing made of Ti alloy either coated with a porous commercially pure Ti [Tri-Lock Plus and Gemini (DePuy)] or with a sintered Ti fiber mesh at the bone-implant interface [Harris/Galante I/II and Trilogy (Zimmer)]. One patient had a metal-backing that was threaded and blasted with hydroxyapatite (Tropic, DePuy); the others were hemispherical and intended for press-fit and/or screw fixation. The liners were conventional ultra-high molecular weight polyethylene (UHMWPE) sterilized by gamma irradiation in air or in an inert atmosphere. The uncemented Ti alloy stem (Profile, DePuy) was in all cases well-fixed and not revised. Additional information about the patients and prosthesis materials was provided by the Norwegian Arthroplasty Register (Table 1).

Histologic evaluation

Periprosthetic tissue samples from the joint capsule, the acetabular membrane, osteolytic lesions, or sites with evidence of metallosis were collected at revision surgery and fixed in 4% buffered formalin. Paraffin-embedded specimens were sectioned to a thickness of 5 µm and stained with haematoxylin and eosin (H&E). Tissue slides from all patients were semi-quantitatively evaluated by two senior pathologists (HKH, PKL) in a blinded fashion using a modified Mirra classification18 described by Doorn et al.19 The intensity was graded as absent (0), low (1+), moderate (2+), or high (3+) (Table 2). Using light microscopy, three high power fields (HPF, 40×) per tissue section with high cellular concentration were counted and graded for acute and chronic inflammatory cells, histiocytes, foreign body giant cells, necrosis, and the amount of metal particles.

Table 2. Modified Mirra Classification Used to Assess Tissue Reactions and Wear Particle Load in Periprosthetic Tissue Samples

Histology	0	1+	2+	3+
Acute inflammatory cells (neutrophils)	0 cells/HPFa	1–5 cells/HPF	6–49 cells/HPF	50 or more/HPF
Mononuclear histiocytes	0 cells/HPF	1–5 cells/HPF	6–49 cells/HPF	50 or more/HPF
Chronic inflammatory cells (lymphocytes, plasma cells, lymphoid follicles)	0 cells/HPF	1–9 cells/HPF	10–49 cells/HPF	50 or more/HPF
Giant cells (multinucleated histiocytes)	0 cells/HPF	1 cell/HPF	2–4 cells/HPF	5 or more cells/HPF
Metal particles	Normal colored histiocytes (no visible, black metal particles per histiocyte)	Slate blue histiocytes (<10 visible, black metal particles per histiocyte)	Dusty black histiocytes (10 to 100 visible, black Metal particles per histiocyte)	Jet black histiocytes (>100 visible, black metal particles per histiocyte)
Necrosis	0 mm of necrosis/slide	1–2 mm of necrosis/slide	3–9 mm of necrosis/slide	>1 cm of necrosis/slide

^a HPF: high power field (×40).

Particle characteristics were measured in the same sections with High-Resolution Optical Darkfield Microscopy (HR-ODM; Auburn, Al) as described by Flatebø et al.20 Using photographs (40×), the total amount of foreign body particles, particle density, equivalent diameter, and circularity (0–1) were determined with image analysis software (NIS-Elements 2.30, Nikon, Japan). Birefringent PE particles were identified by polarization microscopy (40×) and counted in a specified rectangular area with defined steps using a MicroStepperTM stepping stage with the associated software (PetrogLite, Conwy Valley Systems).

Particle isolation for analysis of morphology and chemical composition

Particles were isolated from the tissue samples using a modified enzymatic digestion method.21, 22 All solutions/buffers were sterile-filtered before use. Approximately 0.2 g tissue (wet weight) was sliced into small pieces and washed 4 times with phosphate-buffered saline (PBS; Gibco, 659457), pH 6.8. PBS containing 5 mM l-Cystine (Sigma, C8755) was added and the sample was sonicated at 70% amplitude for 1 min using a VibraCell probe sonicator (Sonics, VCX 130). The tissue was incubated with papain (Sigma, P3125) in a 65°C shaking water bath for 24 h. Following centrifugation (Eppendorf 5810R) at 3220g for 30 min, the pellet was resuspended in an enzyme cocktail containing Proteinase K (MB-1120100), Pronase (Roche, 10165921001), and Collagenase (Roche, 10103586001) and incubated at 37°C for 24 h. After centrifugation, Tris-HCl buffer (Sigma, T5941) containing 20 mg Proteinase K was added to the pellet and the tissue suspension incubated at 55°C for 24 h. Following sonication at 70% amplitude for 1 min, Proteinase K was replenished and the sample was allowed to incubate in a 55°C shaking water bath for 24 h. The enzyme suspension was aspirated, collected in a second tube, and centrifuged at 16.000g for 30 min. The particle suspension was washed with 100% ethanol, diluted 1:20 in water, and sequentially filtered through membrane filters (Whatman, Ø 47 mm) with the pore sizes of 10, 1, 0.1, and 0.02 µm. The isolated particles were observed using a field emission scanning electron microscope (FE-SEM; Supra-55VP, Carl Zeiss AG, Germany) and their chemical composition was determined by energy dispersive X-ray spectroscopy (Thermo Fisher Scientific, MA). The supernatant from the last centrifugation step was ultra-centrifuged (110.000g) to remove any residual particulates and analyzed for ionic Ti and Zr concentration in the tissue samples.

Quantification of metal ion levels in tissue and blood

Whole blood samples (5–10 mL) were taken just prior to revision surgery from the patient's forearm through an intravenous catheter, 1.3 × 4.5 mm (Becton Dickinson Venflon TM Pro, Helsingborg, Sweden) into metal-free, polypropylene tubes (VWR, Oslo, Norway) and stored at −20°C. The concentration of Ti and Zr in blood and enzymatically digested tissue samples were determined by High-Resolution-Inductively Coupled Plasma-Mass Spectrometry (HR-ICP-MS; Element 2 Thermo Finnigan, Bremen, Germany). Prior to metal analysis, an aliquot of ∼1.5 g whole blood or 0.5 mL tissue supernatant was mixed with 3 mL 60% HNO₃ (Merck, Darmstadt, Germany) and 2 mL 30% H₂O₂ (Sigma-Aldrich, Germany) and digested in a microwave-assisted system (Milestone 1200 Mega, Sorisole, Italy). A blank and Seronorm reference blood sample (Sero AS, Oslo, Norway) were treated the same way as the test samples. After digestion, deionized water (MilliQ, Millipore) was added to the samples to a total dilution of 60–70.

Statistical analysis

Statistical analysis was done using GraphPad Prism 6 (GraphPad Software, La Jolla, CA). Data is presented as medians accompanied by an interquartile range (IQR) when the data was skewed, tested with D'Agostino and Pearson omnibus normality test. Otherwise, data is given as means with ranges. The Mann-Whitney U test was used to determine statistical significant differences between the studied groups. Relationships between different parameters were analyzed using Spearman's rho correlation. Results were considered statistically significant when p < 0.05.

Ethics

The project protocol and the biobank have been approved by the Regional Committee for Medical Research Ethics–Western Norway (REK number 2010/2817). The study was performed on coded samples, with written informed consent from every patient prior to blood and tissue sampling.

RESULTS

The mean age at retrieval of the 15 patients in the cemented group was 71 years (50–80 years) and the mean time until revision was 6.5 years (1.5–11.8 years) (Table 1). In the uncemented group, the mean age at retrieval was 65 years (44–78 years) and the mean time until revision was 15.7 years (7–19.3 years). Radiographs illustrating the typical appearance of osteolysis and loosening in each patient group are shown in Figure 1(A,B). Acetabular osteolysis is apparent in Figure 1(A) and osteolysis around the femoral stem is shown in Figure 1(B).

Details are in the caption following the image — **Figure 1**
Open in figure viewer PowerPoint

Radiological images illustrating the reason for revision in both studied patient groups. A: Wear and acetabular osteolysis and/or aseptic loosening of the cup were the reasons for revision in the uncemented group. B: Femoral osteolysis and stem loosening were the reasons for revision in the cemented group.

Histology

Histological tissue examination revealed numerous mononuclear histiocytes, lymphocytes, a few neutrophils and multinucleated giant cells in all patients. These inflammatory cell types were slightly more abundant in tissues associated with the uncemented cups (Table 3). Necrosis, or more specifically coagulative necrosis, which was observed as lighter stained tissue areas, was found to be more prominent in tissues surrounding the cemented stem. Forty seven percent of these cases were graded as 3+, which is the highest grade in the Mirra classification. Diffusely distributed mononuclear histiocytes were the most prominent cell type in the periprosthetic tissues. A histiocytic grade of 3+ was given in 76% of the cases (Table 3). Most histiocytes had ingested or were associated with wear particles, seen as black spots inside/on the cells. Chronic inflammatory cells, that is, lymphocytes, were randomly distributed between the histiocytes and not as abundant as these cells. In some cases (e.g., no. 5 and 15), lymphocytes were found in clusters [Figure 2(A)]. A few, mainly perivascular located neutrophils were found. Multinucleated giant cells with ingested foreign material were observed in 57% of the cases (grade 1+ and 2+) [Figures 2(A,B) and 3].

Table 3. Periprosthetic Tissue Reactions in Patients with Uncemented Metal-Backed Cups and Cemented Titanium Stems

Case No.	Mononuclear Histiocytes	Chronic Inflammatory Cells	Multinucleated Giant Cells	Neutrophils	Metal Particles/Histiocytes	Necrosis
Uncemented
1	2+	3+	0	2+	1+	0
2	3+	2+	2+	1+	2+	2+
3	3+	2+	2+	2+	1+	2+
4	0	0	0	0	0	3+
5	3+	3+	0	2+	1+	2+
6	3+	2+	0	1+	1+	2+
7	3+	2+	1+	2+	1+	3+
8	3+	2+	2+	2+	1+	2+
9	3+	2+	1+	1+	3+	2+
10	3+	2+	2+	2+	2+	0
11	3+	2+	0	2+	0	3+
12	3+	2+	0	1+	1+	1+
13	3+	2+	2+	2+	1+	2+
14	3+	1+	1+	1+	3+	2+
15	3+	3+	2+	2+	1+	1+
Cemented
16	3+	2+	1+	1+	2+	2+
17	0	0	0	0	0	3+
18	0	0	0	0	0	3+
19	0	0	0	0	0	3+
20	3+	2+	1+	1+	2+	1+
21	3+	2+	1+	1+	2+	2+
22	3+	2+	1+	2+	2+	3+
23	3+	2+	1+	2+	2+	2+
24	2+	1+	0	1+	1+	2+
25	3+	2+	0	1+	2+	3+
26	3+	2+	0	1+	2+	1+
27	3+	2+	1+	1+	2+	2+
28	3+	2+	1+	1+	1+	2+
29	2+	1+	0	1+	1+	3+
30	3+	2+	1+	1+	2+	3+

Uncemented cups: tissue samples were taken from the joint capsule and/or the acetabular membrane; cemented stems: tissue samples were taken from the proximal femur, distal femur, or the femur channel.

Particle analysis

Different microscopy techniques and energy-dispersive X-ray analysis (Figure 4) indicated that implant wear products originated from different sources. Tissues around cemented stems contained mainly submicron ZrO₂ particles, originating from bone cement degradation, but also some Ti alloy particles worn off from the stem. Particles containing pure Ti and Ti alloy elements were most abundant in tissues adjacent to the uncemented cups. A higher particle load (median cemented = 14,727 particles/mm², IQR = 17,019 vs. median uncemented = 1519 particles/mm², IQR = 3776; p < 0.001) was found in tissues adjacent to cemented stems (Table 4). Image analysis revealed particle equivalent diameters in the range of 0.12–6.46 µm in the uncemented group, with >50% of the particles being ≤ 0.4 µm (Figure 5). The median equivalent diameter of particles (0.42 µm and IQR = 0.1) was smaller than in the cemented group (0.55 µm, IQR = 0.185, and p = 0.034). The observed ZrO₂ particles were more uniform in their round shape than the Ti and Ti alloy particles, which had a more polygonal shape.

Table 4. Particle Characterization Using Digital Images (40× Magnification) of Periprosthetic Tissues from Patients with Uncemented Metal-Backed Cups and Cemented Titanium Stems

Case No.	Particle Density (per mm²)	Median Equivalent Diameter (µm)	Median Circularity	PE density (per mm²)
Uncemented
1	1413	0.57	0.85	1.7
2	14,719	0.36	N/A	1.9
3	1626	0.42	0.95	27.8
4	8114	0.42	1	11.5
5	2641	0.36	1	0.6
6	117	0.47	0.82	0
7	1214	1.05	0.92	7.3
8	5357	0.36	1	3.0
9	N/A	N/A	N/A	23.6
10	1338	0.42	1	4.4
11	69	2.6	N/A	0.2
12	3827	0.52	0.98	24.9
13	185	0.56	N/A	1.7
14	8937	0.42	N/A	1.4
15	1193	0.45	1	2.8
Cemented
16	6897	0.59	N/A	0.6
17	14,922	0.47	N/A	3.6
18	13,041	0.51	N/A	2.8
19	14,727	0.51	N/A	3.0
20	9878	0.51	N/A	2.4
21	32,428	0.51	N/A	2.1
22	3664	0.55	N/A	0.2
23	21,098	1.05	0.86	4.9
24	14,164	0.7	1	0.8
25	9610	0.7	0.83	0
26	33,619	0.51	N/A	0
27	42,675	0.69	N/A	0.2
28	7902	0.42	1	0.3
29	35,592	0.73	0.95	0.9
30	14,987	0.6	0.9	0.3

N/A: Particle characteristic could not be measured appropriately.
Images were taken with High-Resolution Optical Darkfield Microscopy (HR-ODM). Total number of particles, particle density, median equivalent diameter, and median circularity were measured using NIS Elements image analysis software. Polyethylene particles (PE) were counted (total number and particle density) using a polarization microscope with a motorized table.

Polyethylene particles (PE) (Figure 6) were found in almost all tissue samples and were generally more abundant in the tissues adjacent to the uncemented cups (median uncemented = 2.8 PE/mm², IQR = 8.1 vs. median cemented = 0.8 PE/mm², IQR = 2.4, and p = 0.053). The PE particles accounted only for a small portion of total number of particles in all samples (8% around uncemented cups, 0.24% around cemented stems). The size of PE particles ranged from submicron to over 100 µm along one dimension. Large PE particles (>100 µm) were in some cases associated with giant cells (p = 0.291).

In tissues around cemented stems, the total number of particles positively correlated with the amount of mononuclear histiocytes (r = 0.92, p < 0.001), chronic inflammatory cells (r = 0.92, p < 0.001), multinucleated giant cells (r = 0.63, p = 0.036), and neutrophils (r = 1.00, p<0.001). A similar trend was also observed in the tissues surrounding the uncemented cups (ns).

Metal ion analysis

The median Ti concentrations in whole blood samples in patients with loose cemented stems (n = 10) and loose uncemented cups (n = 13) were 10.5 µg/L (IQR = 6.1) and 21.1 µg/L (IQR = 71.2), respectively (p = 0.73) [Figure 7(A)]. In uncemented cases with high abrasive wear and metallosis, Ti concentrations over 100 µg/L were detected. The median Zr concentrations in blood in patients with loose cemented stems (n = 10) and loose uncemented cups (n = 13) were 1.87 µg/L (IQR = 0.64) and 0.37 µg/L (IQR = 0.56), respectively, (p = 0.002) [Figure 7(B)]. The concentrations of Ti (r = 0.77 and p = 0.024) and Zr (r = 0.71 and p = 0.044) in whole blood were proportional to the number of wear particles/mm² in the tissue sections. The ionic Ti and Zr concentrations in the enzymatically digested periprosthetic tissues were 10 to 100 times higher than in the blood samples: The two samples from the cemented group showed, as expected, the highest Zr concentration (82.6 and 166.6 µg/L), compared with the sample from the uncemented group (11.6 µg/L). Ti concentrations were 1284 and 1405.8 µg/L in the cemented cases and 329.2 µg/L in the uncemented case.

DISCUSSION

Implant wear and associated immune reactions to wear debris are considered to be an important factor in the onset of osteolysis and aseptic loosening of hip implants. Previous studies have shown that the accumulation of submicron and micron-sized wear debris initiates a foreign body inflammatory reaction, which includes the activation of histiocytes (tissue macrophages) and the influx of other immune cells like lymphocytes and neutrophils.23, 24 The presence of neutrophils in our analyzed tissue samples suggests that newly generated wear debris induced acute inflammatory responses in the soft tissue adjacent to the implant. The apparent, relatively strong pronounced coagulative necrosis (>80% of the tissue samples had a grade of 2+ and more) could be a sign of hypersensitivity.25

The continuous production of wear debris, activation of macrophages, ingestion of wear debris, and release of proinflammatory cytokines and other mediators can cause inflammatory-mediated morphological changes in the tissue, which contribute to osteolysis and implant loosening. In this study, we have shown that the periprosthetic tissues of patients with revised Ti-based hip implants contain various types of metallic degradation products, bone cement debris and PE particles, which all might have contributed to the inflammatory tissue responses we have observed.

It has been proposed that local periprosthetic tissue inflammation is affected by particle characteristics, like particle size,26 load, shape and chemical reactivity.1 Hallab et al. suggested that the local inflammatory response is proportional to the particle load in the tissue.1 We found a positive correlation between the histological grade of the tissue responses and the total number of particles. All tissue samples had a high particle load. Tissues around the cemented stems contained 10 fold more particles than the tissues around the cups, but both patient cohorts were sufficiently exposed to wear debris to induce foreign body reactions.

The ZrO₂ particles, which originated from bone cement degradation, are extremely hard ceramic particles that are embedded as agglomerates in the bone cement matrix. The primary particles retain their uniform size and round or ovoid shape during wear processes. We found these particles relatively dispersed in the tissue, mostly internalized by histiocytes. Particles found in tissues from the uncemented cases were often polygonal and varied more in size, which may be attributed to different wear processes. Larger, pure Ti fragments were possibly broken off from the metal-backing moving against the bone, while smaller particles were probably generated when the femoral head wore through the PE-liner into the Ti alloy cup. Both ZrO₂ and Ti-based wear debris were of submicron size. Cellular uptake and thus cellular responses to wear debris is affected by particle size. Nanometer- and submicron-sized particles are generally taken up by phagocytic cells through various endocytic pathways. The uptake of metal particles <150 nm was found to be mediated through receptor-mediated endocytosis and pinocytosis.27 Larger particles (>100 µm) are not as easily ingested as smaller particles by phagocytic cells. In response, tissue macrophages may fuse to form multinucleated giant cells. These multinucleated giant cells may not only have formed in the attempt to ingest larger particles, but also to cope with the enormous amount of smaller particles observed in the tissue samples.

In addition to ZrO₂ and Ti-based particles, we also identified PE particles in the tissue samples using polarized light microscopy. These particles had an irregular shape and ranged from micron (≥1 µm) to larger, spindle-shaped particles (>100 µm) that were partially associated with multinucleated giant cells. In vitro studies have shown that exposure to PE particles within the phagocytic size range (0.1–10 µm) results in activation of macrophages,28, 29 leading to release of cytokines that modulate osteoclast activation and osteolysis. In this study large PE particles (>100 µm) were in some cases observed within giant cells, but the total amount of PE particles did not correlate with the number of giant cells, which is in contrast to the findings by Ito et al.30 However, in our study the observed number of PE particles accounted unexpectedly only for a small portion of the total number of particles. This might be due to detection limitations with the polarized microscopy technique and most probably not due to sampling bias, since the tissue samples were taken from the joint capsule or the fibrous tissue behind the cup or osteolytic lesions. In the cemented cases, the PE cups were intact and the wear minor. In contrast, all liners from the uncemented cups were worn, although it must be noted that these cups failed quite late (Table 1). In a post mortem retrieval study, Urban et al. characterized some well functioning uncemented acetabular components (Harris-Galante I) after a mean of eleven years in situ, but with particle induced granulomas and progression of osteolysis.17

Implant-derived metal ions have been shown to contribute to the mechanism of osteolysis by increasing bone resorption and osteoclast differentiation in vitro.14, 15 Elevated concentrations of metal ions were measured in human body fluids and tissue samples from THR patients.11, 12 Dorr et al.11 found Ti-concentrations ranging from 38 to 602 µg/L in the blood from subjects with osteolysis around Ti alloy implants, which is in line with our findings. It is expected that the metal ion concentrations in the periprosthetic tissues were 100–1000 fold higher than in the blood stream. Compared with previous findings11, 31 our estimates show slightly lower metal ion concentrations in the tissue samples from related retrievals. This might be due to methodological differences between the studies. A method for separation and quantification of particle debris and ionic forms in tissue samples was developed in this study. We suggest that our method better separates between particulate metal debris and soluble forms. However, only a limited number of samples were analyzed, so further validation is necessary.

To our knowledge, there are only a few methods available in the literature to precisely quantify and speciate particulate debris and ionic forms.32, 33 Thus, the precise metal ion concentration in tissue samples surrounding hip implants still remains unclear. There is evidence that the osteolytic effect of metal ions might have been underestimated in previous studies. It is therefore necessary to further study the exact role of metal ions in the mechanism of osteolysis around Ti-based hip implants. In summary, we conclude that different types of wear debris induced a similar inflammatory response in tissues adjacent to Ti-based hip implants revised for wear, osteolysis and/or loosening. Particle size, load, and metal ions might be more important factors than particle composition in the onset of inflammatory tissue responses eventually leading to osteolysis.

ACKNOWLEDGMENTS

The authors thank Irene Ohlen Moldestad (retrieval handling and analysis), Anne Aarsand (histological tissue preparation at Dept. of Clinical Medicine, UiB), Egil S. Ericksen (SEM-analysis at Laboratory for Electron Microscopy, UiB), and Siv Hjorth Dundas (ICP-MS-analysis at Dept. of Earth Science, UiB) for their excellent technical support. Further, they thank the surgeons that contributed with retrieval samples.

REFERENCES

1Hallab NJ, Jacobs JJ. Biologic effects of implant debris. Bull NYU Hosp Jt Dis 2009; 67: 182–188.
PubMed Google Scholar
2Ollivere B, Wimhurst JA, Clark IM, Donell ST. Current concepts in osteolysis. J Bone Joint Surg Br 2012; 94B: 10–15.
10.1302/0301-620X.94B1.28047
Web of Science® Google Scholar
3Noordin S, Masri B. Periprosthetic osteolysis: Genetics, mechanisms and potential therapeutic interventions. Can J Surg 2012; 55: 408–417.
10.1503/cjs.003711
PubMed Web of Science® Google Scholar
4von Domarus C, Rosenberg JP, Ruther W, Zustin J. Necrobiosis and T-lymphocyte infiltration in retrieved aseptically loosened metal-on-polyethylene arthroplasties. Acta Orthop 2011; 82: 596–601.
10.3109/17453674.2011.625534
PubMed Google Scholar
5Huber M, Reinisch G, Trettenhahn G, Zweymüller K, Lintner F. Presence of corrosion products and hypersensitivity-associated reactions in periprosthetic tissue after aseptic loosening of total hip replacements with metal bearing surfaces. Acta Biomater 2009; 5: 172–180.
10.1016/j.actbio.2008.07.032
CAS PubMed Web of Science® Google Scholar
6Campbell P, Ebramzadeh E, Nelson S, Takamura K, De Smet K, Amstutz HC. Histological features of pseudotumor-like tissues from metal-on-metal hips. Clin Orthop Relat Res 2010; 468: 2321–2327.
10.1007/s11999-010-1372-y
PubMed Web of Science® Google Scholar
7Urban RM, Tomlinson MJ, Hall DJ, Jacobs JJ. Accumulation in liver and spleen of metal particles generated at nonbearing surfaces in hip arthroplasty. J Arthroplasty 2004; 19(8 Suppl 3): 94–101.
10.1016/j.arth.2004.09.013
PubMed Web of Science® Google Scholar
8Willert HG, Broback LG, Buchhorn GH, Jensen PH, Koster G, Lang I, Ochsner P, Schenk R. Crevice corrosion of cemented titanium alloy stems in total hip replacements. Clin Orthop Relat Res 1996: 51–75.
PubMed Web of Science® Google Scholar
9Cadosch D, Chan E, Gautschi OP, Filgueira L. Metal is not inert: Role of metal ions released by biocorrosion in aseptic loosening-current concepts. J Biomed Mater Res A 2009; 91: 1252–1262.
10.1002/jbm.a.32625
CAS PubMed Web of Science® Google Scholar
10Agins HJ, Alcock NW, Bansal M, Salvati EA, Wilson PD, Jr., Pellicci PM, Bullough PG. Metallic wear in failed titanium-alloy total hip replacements. A histological and quantitative analysis. J Bone Joint Surg Am 1988; 70: 347–356.
10.2106/00004623-198870030-00005
CAS PubMed Web of Science® Google Scholar
11Dorr LD, Bloebaum R, Emmanual J, Meldrum R. Histologic, biochemical, and ion analysis of tissue and fluids retrieved during total hip arthroplasty. Clin Orthop Relat Res 1990: 82–95.
CAS PubMed Web of Science® Google Scholar
12Jacobs JJ, Skipor AK, Patterson LM, Hallab NJ, Paprosky WG, Black J, Galante JO. Metal release in patients who have had a primary total hip arthroplasty. A prospective, controlled, longitudinal study. J Bone Joint Surg Am 1998; 80: 1447–1458.
10.2106/00004623-199810000-00006
CAS PubMed Web of Science® Google Scholar
13Kunze J, Koelling S, Reich M, Wimmer MA. Use of ultrasonic nebulizer with desolvator membrane for the determination of titanium and zirconium in human serum by means of inductively coupled plasma-mass spectroscopy. Fresenius J Anal Chem 2000; 366: 165–166.
10.1007/s002160050031
CAS PubMed Web of Science® Google Scholar
14Cadosch D, Chan E, Gautschi OP, Meagher J, Zellweger R, Filgueira L. Titanium IV ions induced human osteoclast differentiation and enhanced bone resorption in vitro. J Biomed Mater Res A 2009; 91: 29–36.
10.1002/jbm.a.32183
CAS PubMed Web of Science® Google Scholar
15Niki Y, Matsumoto H, Suda Y, Otani T, Fujikawa K, Toyama Y, Hisamori N, Nozue A. Metal ions induce bone-resorbing cytokine production through the redox pathway in synoviocytes and bone marrow macrophages. Biomaterials 2003; 24: 1447–1457.
10.1016/S0142-9612(02)00531-8
CAS PubMed Web of Science® Google Scholar
16Wang JY, Wicklund BH, Gustilo RB, Tsukayama DT. Titanium, chromium and cobalt ions modulate the release of bone-associated cytokines by human monocytes/macrophages in vitro. Biomaterials 1996; 17: 2233–2240.
10.1016/0142-9612(96)00072-5
CAS PubMed Web of Science® Google Scholar
17Urban RM, Hall DJ, Della Valle C, Wimmer MA, Jacobs JJ, Galante JO. Successful long-term fixation and progression of osteolysis associated with first-generation cementless acetabular components retrieved post mortem. J Bone Joint Surg Am 2012; 94: 1877–1885.
10.2106/JBJS.J.01507
PubMed Web of Science® Google Scholar
18Mirra JM, Amstutz HC, Matos M, Gold R. The pathology of the joint tissues and its clinical relevance in prosthesis failure. Clin Orthop Relat Res 1976: 221–240.
PubMed Web of Science® Google Scholar
19Doorn PF, Mirra JM, Campbell PA, Amstutz HC. Tissue reaction to metal on metal total hip prostheses. Clin Orthop Relat Res 1996(329 Suppl): S187–205.
10.1097/00003086-199608001-00017
CAS PubMed Web of Science® Google Scholar
20Flatebø RS, Høl PJ, Leknes KN, Kosler J, Lie SA, Gjerdet NR. Mapping of titanium particles in peri-implant oral mucosa by laser ablation inductively coupled plasma mass spectrometry and high-resolution optical darkfield microscopy. J Oral Pathol Med 2011; 40: 412–420.
10.1111/j.1600-0714.2010.00958.x
CAS PubMed Web of Science® Google Scholar
21Maloney WJ, Smith RL, Schmalzried TP, Chiba J, Huene D, Rubash H. Isolation and characterization of wear particles generated in patients who have had failure of a hip arthroplasty without cement. J Bone Joint Surg Am 1995; 77: 1301–1310.
10.2106/00004623-199509000-00002
CAS PubMed Web of Science® Google Scholar
22Wirth MA, Agrawal CM, Mabrey JD, Dean DD, Blanchard CR, Miller MA, Rockwood CA, Jr. Isolation and characterization of polyethylene wear debris associated with osteolysis following total shoulder arthroplasty. J Bone Joint Surg Am 1999; 81: 29–37.
10.2106/00004623-199901000-00005
CAS PubMed Web of Science® Google Scholar
23Gallo J, Goodman SB, Konttinen YT, Raska M. Particle disease: Biologic mechanisms of periprosthetic osteolysis in total hip arthroplasty. Innate Immun 2013; 19: 213–214.
10.1177/1753425912451779
CAS PubMed Web of Science® Google Scholar
24Day JS, Baxter RM, Ramsey ML, Morrey BF, Connor PM, Kurtz SM, Steinbeck MJ. Characterization of wear debris in total elbow arthroplasty. J Shoulder Elbow Surg. 2013; 22: 924–931.
10.1016/j.jse.2013.02.001
PubMed Web of Science® Google Scholar
25Willert HG, Buchhorn GH, Fayyazi A, Flury R, Windler M, Koster G, Lohmann CH. Metal-on-metal bearings and hypersensitivity in patients with artificial hip joints - A clinical and histomorphological study. J Bone Joint Surg Am 2005; 87A: 28–36.
10.2106/JBJS.A.02039pp
Web of Science® Google Scholar
26Matthews JB, Besong AA, Green TR, Stone MH, Wroblewski BM, Fisher J, Ingham E. Evaluation of the response of primary human peripheral blood mononuclear phagocytes to challenge with in vitro generated clinically relevant UHMWPE particles of known size and dose. J Biomed Mater Res 2000; 52: 296–307.
10.1002/1097-4636(200011)52:2<296::AID-JBM8>3.0.CO;2-9
CAS PubMed Web of Science® Google Scholar
27Keegan GM, Learmonth ID, Case CP. Orthopaedic metals and their potential toxicity in the arthroplasty patient: A review of current knowledge and future strategies. J Bone Joint Surg Br 2007; 89: 567–573.
10.1302/0301-620X.89B5.18903
CAS PubMed Web of Science® Google Scholar
28Matthews JB, Green TR, Stone MH, Wroblewski BM, Fisher J, Ingham E. Comparison of the response of primary human peripheral blood mononuclear phagocytes from different donors to challenge with model polyethylene particles of known size and dose. Biomaterials 2000; 21: 2033–2044.
10.1016/S0142-9612(00)00089-2
CAS PubMed Web of Science® Google Scholar
29Ingham E, Fisher J. The role of macrophages in osteolysis of total joint replacement. Biomaterials 2005; 26: 1271–1286.
10.1016/j.biomaterials.2004.04.035
CAS PubMed Web of Science® Google Scholar
30Ito S, Matsumoto T, Enomoto H, Shindo H. Histological analysis and biological effects of granulation tissue around loosened hip prostheses in the development of osteolysis. J Orthop Sci 2004; 9: 478–487.
10.1007/s00776-004-0808-1
PubMed Web of Science® Google Scholar
31Hallab NJ, Mikecz K, Vermes C, Skipor A, Jacobs JJ. Orthopaedic implant related metal toxicity in terms of human lymphocyte reactivity to metal-protein complexes produced from cobalt-base and titanium-base implant alloy degradation. Mol Cell Biochem 2001; 222: 127–136.
10.1023/A:1017979710992
CAS PubMed Web of Science® Google Scholar
32Hart AJ, Quinn PD, Sampson B, Sandison A, Atkinson KD, Skinner JA, Powell JJ, Mosselmans JF. The chemical form of metallic debris in tissues surrounding metal-on-metal hips with unexplained failure. Acta Biomater 2010; 6: 4439–4446.
10.1016/j.actbio.2010.06.006
CAS PubMed Web of Science® Google Scholar
33Goode AE, Perkins JM, Sandison A, Karunakaran C, Cheng H, Wall D, Skinner JA, Hart AJ, Porter AE, McComb DW, et al. Chemical speciation of nanoparticles surrounding metal-on-metal hips. Chem Commun (Camb) 2012; 48: 8335–8337.
10.1039/c2cc33016d
CAS PubMed Web of Science® Google Scholar

Citing Literature

Volume103, Issue3

April 2015

Pages 709-717

Wear particles and ions from cemented and uncemented titanium-based hip prostheses—A histological and chemical analysis of retrieval material

Abstract

INTRODUCTION