On the glow curves and TL centres in CaF2:Ce, Mn crystals irradiated by cathode rays
Abstract
enThermoluminescence of single crystals of CaF2:Ce, Mn irradiated by low energy (10 kV) cathode rays is investigated in the temperature range 28 to 250°C. The results indicate that the electron traps responsible for the low temperature (up to 260°C) glow peaks and the high temperature (260 to 500°C) peaks are distinctly different. Peaks occurring upto 260°C are due to Ce2+ ions present in two site symmetries – cubic and tetragonal. Those occurring in the high temperature range are due to intrinsic electron traps stabilised by lattice imperfections caused by impurity ions. In these crystals, for all the glow peaks the holes are the mobile species.
Abstract
deEs wird die Thermolumineszenz von CaF2:Ce, Mn-Einkristallen untersucht, die mit Niederenergie-(10 kV)-Kathodenstrahlen im Temperaturbereich von 28 bis 250°C untersucht werden. Die Ergebnisse zeigen, daß die für die Glowmaxima bei tiefen Temperaturen (bis 260°C) und die für hohe Temperaturen verantwortlichen Haftstellen wesentlich unterschiedlich sind. Die Maxima, die bis zu 260°C auftreten, werden durch Ce2+-Ionen hervorgerufen, die an zwei Symmetrieplätzen – kubisch und tetragonal – vorhanden sind. Die-jenigen, die im Hochtemperaturbereich auftreten, werden durch intrinsische Elektronen-haftstellen hervorgerufen, die durch Fremdionen erzeugte Gitterfehler stabilisiert werden. In diesen Kristallen sind für alle Glowmaxima die Löcher die mobilen Ladungsträger.