Structure of microporous polypropylene sheets containing CaCO₃ filler

The microporous polypropylene sheets were prepared by biaxially stretching polypropylene sheets containing CaCO₃ filler (particle size, 0.08–3.0 μm), when the CaCO₃ filler content was 59% by weight and the stretching ratio was 2.8 × 1.8. The microstructure of the sheets were investigated in relation to the CaCO₃ particle size by a N₂ gas permeation method. (1) Effective porosity increases with decreasing mean particle size of filler. (2) The tortuosity factor of the pore is in the range of 25–40 and becomes relatively smaller with decreasing mean particle size of filler. (3) The equivalent pore size becomes relatively smaller with decreasing mean particle size of filler.