Modelling the polymerization of 1,3-butadiene in solution with a neodymium catalyst
Abstract
enThe batch polymerization of butadiene in hexane with an in-situ-activated Ziegler-Catalyst containing neodymium versatate, ethylaluminium sesquichloride and triisobutylaluminium was studied at 45°C. The rate of polymerization was determined by online density measurements. A mathematical model has been developed which is able to describe the kinetics of polymerization at different catalyst ratios. At molar ratios of aluminium/neodymium above 40 a bimodal molar mass distribution can be observed by gel permeation chromatography which leads to the assumption of more than one active species being present in the polymerization system.
Abstract
deDie diskontinuierliche Polymerisation von Butadien in Hexan bei 45°C mit einem in-situ-aktivierten Ziegler-Katalysator aus Neodymversatat, Ethylaluminiumsesquichlorid und Triisobutylauminium wurde untersucht. Die Polymerisationsgeschwindigkeit wurde durch Dichtemessungen verfolgt. Zur Beschreibung der Polymerisationskinetik bei verschiedenen Katalysatorzusammensetzungen wurde ein mathematisches Modell entwickelt. Bei einem molaren Aluminium/Neodym-Verhältnis über 40 kann mittels Gelpermeationschromatographie eine bimodale Molmassenverteilung beobachtet werden, was zu der Annahme führt, daß im Polymerisationssystem mehr als eine aktive Spezies anwesend ist.